SMALL-GRAIN CONCRETE BASED ON METALLURGY WASTE

The paper presents the approach to the metallurgical waste recycling introducing them into the composition of fine-grained concretes. Blast-furnace produced by OOO „EVRAZ ZSMK‟ is used as a recyclable waste. According to the X-ray diffraction patterns, the blast-furnace is mainly represented by such components as iron and calcium hydrated silicates, quartz, calcite and carbon. It is found that during the hydrothermal treatment of fine-grained concrete, carbonate-containing additives facilitate the formation of hydrated calcium silicates containing carbonate groups the composition of which is close to the that of hydrosilicate phases. The formation of these products in the concrete production contributes to the strength properties improvement in the material obtained and reduces the possibility of late formation of similar phases during its service. This minimizes the carbon dioxide corrosion and shrinkage deformation accompanying this process. It is shown that the use of blast-furnace as fine aggregate in the concrete mix increases the material density and strength by 14 % and 11.2 %, respectively. The water absorption decreases by 5 %, which positively affects the frost resistance of finegrained concretes. The obtained fine-grained concrete provide can be used to produce the M250 concrete grade.

industrial waste, construction materials, concrete, recycling, blastfurnace

1. Skripnikova N.K., Yuryev I.Yu., Litvinova V.A., Kosmachev P.V., Semenovykh M.A. Ispol'zovanie zoloshlakovykh otkhodov dlya polucheniya razlichnykh vidov stroitel'nykh materialov [The use of ash and slag waste for production of various types of building materials]. Stroitel'nye materialy. 2015. No. 1. Pp. 1–4. (rus)

2. Fedosov S.V., Shchepochkina Yu.A., Rumyantseva V.E. et al. Vtorichnye material'nye resursy dlya stroitel'noi industrii [Secondary material resources for construction industry]. Ivanovo: IVGPU. 2017. 188 p. (rus)

3. Dvorkin L.I., Dvorkin O.L. Stroitel'nye materialy iz otkhodov promyshlennosti [Building materials from industrial waste]. Rostov-on-Don: Feniks, 2007. 369 p. (rus)

4. Bazhenov Yu.M. Tekhnologiya betona [Concrete technology]. Moscow: ASV, 2003. 500 p. (rus)

5. Valeev R.Sh., Shaikhiev I.G. Utilizatsiya shlamovykh otkhodov teploenergeticheskikh tsentralei pri proizvodstve stroitel'nykh materialov [Sludge waste from thermal power plants in building materials production]. Ekologiya i promyshlennost' Rossii. 2010. No. 2. Pp. 28–29. (rus)

6. Skripnikova N.K., Kosmachev P.V., Shekhovtsov V.V., Volokitin O.G., Semenovykh M.A., Vliyanie nanorazmernogo poroshka dioksida kremniya na obzhigovye stroitel''nye materialy s ispol''zovaniem metallurgicheskikh otkhodov [Fired building materials manufactured by adding silica nanopowder]. Vestnik Tomskogo gosudarstvennogo arkhitekturno-stroitel'nogo universiteta – Journal of Construction and Architecture. 2018. V. 20. No. 2. Pp.150–156. (rus)

7. Panova V.F. Tekhnogennye produkty kak syr'e dlya stroiindustrii [Technogenic products as raw materials for construction industry]. Novokuznetsk: SibGIU, 2009. 289 p. (rus)

8. Kozlova V.K., Karpova Yu.V., Manokha A.M. Sostav alyuminatno-alyumoferritnykh faz i ikh produkty gidratatsii v razlichnykh tsementakh i smeshannykh vyazhushchikh. Chast' I. Sostav alyuminatov, alyumoferritov i ferritov kal'tsiya i ikh produkty gidratatsii v razlichnykh usloviyakh [Composition of aluminate-alumoferrite phases and their hydration products in various cements and mixed binders. Part I. Composition of aluminates, alumoferrites and calcium ferrites and their hydration products under various conditions]. Barnaul, 2008. 302 p. (rus)

9. Trambovetsky V.P. Beton v sovremennom stroitel'stve [Concrete in modern construction]. Tekhnologii betonov. 2006. No. 2. Pp. 72-74. (rus)

10. Buravchuk N.I. Ispol'zovanie tekhnogennogo syr'ya v tekhnologii betonov [Use of man-made raw materials in technology of concrete]. Proc. Int. Sci. Conf. „World Science‟. Kirov, 2016. Pp. 34–45. (rus)